FeatUres

  • Wipe Clean
  • LEAD and Heavy Metal Free
  • High Abrasion Resistance
  • VOC Compliant
  • Water and Dust Proof
  • High Bally Flex rating
  • Fire Retardant
  • Color Fastness
  • Customized Textures
  • REACH Compliant
  • High Temperature Resistance

Specifications

SHEET PVC INSULATION MATT
Specification: IS 15652 :2006 Thickness: 2.00MM , 3MM

  • Shape 6.1 2 mm: Should be specific shape or R oll 3mm: Should be specific shape or R oll
    Leakage Current 8.2.2 (Μa) 2 mm: 10 mA Max
    3mm: 10 mA Max.
  • Dimensions 6.2 (Mm) Length
    2 mm: Should be 1000 mm + 20 mm Should be 1000 mm + 20 0r in o ther width agreement

    with purchaser
    3mm: Should be 1000 mm + 20 mm Should be 1000 mm + 20 0r in o ther width agreement with purchaser

    Aging Properties (70+10c)For 168 H Tensile strength
    2 mm: 75 % OF corresponding value of same lot sample without conditioning
    3mm: 75 % OF corresponding value of same lot sample without conditioning

    Elongation
    2 mm: 75 % OF corresponding value of same lot sample without conditioning
    3mm: 75 % OF corresponding value of same lot sample without conditioning
  • Thickness 6.3(mm) 2 mm: 2.00 mm + 10 %
    3mm: 3.00 mm + 10 %
    Ac Proof Voltage 8.2.4 (kv) 2 mm: 10 Kv
    3mm: 36 Kv
  • Tensile Strength 8.1 (n/mm²) 2 mm: 15 (-10 to 15 0C ) 12 (-40 to 27 0C )
    3mm: 15 (-10 to 15 0C ) 12 (-40 to 27 0C )
    Thermal Flame Retardence 8.2.1(Second) 2 mm: 5 s after removal of blue flame
    3mm: 5 s after removal of blue flame
  • Elongation 8.1 (%) 2 mm: 15 (-10 to 15 0C ) 12 (-40 to 27 0C )
    3mm: 15 (-10 to 15 0C ) 12 (-40 to 27 0C )
    Acid /Alkalis And Oil Resistance 8.5 (n/mm²) (Acid Resistance) Tensile strength Elongation
    3mm: 80 % OF corresponding value of same lot sample without conditioning

    (Alkalis Resistance)Tensile strength Elongation
    2mm: 80 % OF corresponding value of same lot sample without conditioning
    3mm: 80 % OF corresponding value of same lot sample without conditioning

    (Oil Resistance)Tensile strength Elongation
    2mm: 80 % OF corresponding value of same lot sample without conditioning
  • Insulation Resistance 8.2.1(MΩ) 2 mm: 100000M Ω(5000 V megger)1000000M Ω(500 V megger)
    3mm: 100000M Ω(5000 V megger) 1000000M Ω(500 V megger)
    Ac Di Electric Strength 8.2.3 (Kv) 2 mm: 30 Kv
    3mm: 65 Kv