TECHNICAL SPECIFICATION SHEET ENDURA FLOORING
Specification / Drawing: IS : 3462 /1986, Material: ENDURA FLOORING, Dimension: 1.50mm, 2mm, 3mm

• Visual Observation (mm)IS: 2076 1.5mm: Should be free from pin holes, blisters, porosity & visual defects
  2mm: Should be free from pin holes, blisters, porosity & visual defects.
  Color Fastness To Day Light (%)IS: 2076 1.5mm: The Color Fastness correspond to at least standard No. 4
  2mm: The Colour Fastness correspond to at least standard No. 4
  3mm: The Colour Fastness correspond to at least standard No. 4
• Thickness(mm) 1.5mm: The mean thickness shall no t differ by morethan 0.13 mm from that specified
  2mm: The mean thickness shall no t differ by more than0.13 mm from that specified
  3mm: The mean thickness shall no t differ by more than0.13 mm from that specified
  
  Variation in Thickness(mm)
  1.5mm: The variation between any two measurementsshall not exceed 0.20 mm
  2mm: The variation between any two measurementsshall not exceed 0.20 mm
  3mm: The variation between any two measurementsshall not exceed 0.20 mm
  
  Width(mm)%
  1.5mm: Shall not be less then that specified and not 6 mm more then that specified
  2mm: Shall not be less then that specified and not 6 mm more then that specified
  3mm: Shall not vary from the declared dimensions by more than 0.13% or + 0.4 mm whiche ver is less
  Moisture Movement (%)IS: 2076 Machine direction (%)
  1.5mm:Change in any linear dimensions shall no t exceed 0.4 percent.
  2mm: Change in any linear dimensions shall no t exceed 0.4 percent.
  3mm: Change in any linear dimensions shall no t exceed 0.4 percent
  
  Transverse direction (%)
  1.5mm:Change in any linear dimensions shall no t exceed 0.4 percent.
  2mm: Change in any linear dimensions shall no t exceed 0.4 percent.
  3mm: Change in any linear dimensions shall no t exceed 0.4 percent.
• Residual Indentation (mm) 1.5mm: Shall not exceed 0.10 mm
  2mm: Shall not exceed 0.10 mm
  3mm: Shall not exceed 0.10 mm
  Heat Ageing And Exudation (At 700c For 15 Days) 1.5mm: No exudation of plasticizer shall be apparent nor shall there be any change in appearance. The mandrel test shall no t produce surface cracking
  
  2mm: No exudation of plasticizer shall be apparent nor shall there be any change in appearance. The mandrel test shall no t produce surface cracking
  
  3mm: No exudation of plasticizer shall be apparent nor shall there be any change in appearance. The mandrel test shall no t produce surface cracking
• Flexibility (00c For 60 Minutes) 1.5mm: Shall not break crack or show any other signs of failure
  2mm: Shall not break crack or show any other signs of failure
  3mm: Shall not break crack or show any other signs of failure
  Elastic Product ((mj/m3) 1.5mm: The mean product of tensile strength and elongation shall be not less than 2MJ/m3
  2mm: The mean product of tensile strength and elongation shall be not less than 2MJ/m3.
  3mm: The mean product of tensile strength and elongation shall be not lessthan 2MJ/m3.
• Ply Adhesion (kn/m) 1.5mm: Adhesion between plies in any test piece shall not be less than 1.05 KN/m.
  2mm: Adhesion between plies in any test piece shall not be less than 1.05 KN/m.
  3mm: Adhesion between plies in any test piece shall not be less than 1.05 KN/m
  Flammability ((mj/m3) 1.5mm: Class B
  2mm: Class B
• Marking 3mm: Firm’s identification code, Thickness, Width, Shade
  Abrasion Resistance 1.5mm: 0.35 cm3 as per IS:9532
  2mm: 0.35 cm3 as per IS:9532
• Dimensional Stability (%) Machine direction(mm)
  1.5mm: Change in any linear dimension
  2mm: Change in any linear dimension
  3mm: Change in any linear dimension
  
  Transverse direction (%)
  1.5mm: Shall not exceed 0.40 percent
  2mm: Shall not exceed 0.40 percent.
  3mm: Shall not exceed 0.40 percent
  
  Visual Inspection (%)
  1.5mm: After the test the specimen shall sho w no signs of curling.
  2mm: After the test the specimen shall sho w no signs of curling.
  3mm: After the test the specimen shall sho w no signs of curling
  Resistance To Various Substances Iso propyl alcohol
  3mm: The average scratch width obtained after.immersion shall notexceed 2.0 mm
  Light mineral oil
  Cotton seed oil
  NaOH solution 2%
  Iso propyl alcohol
  3mm: The Color of the treated pieces shall show no significant change when compared with untreated material
• Curling (mm) 1.5mm: Shall not exceed 0.75 mm
  2mm: Shall not exceed 0.75 mm
  3mm: Shall not exceed 0.75 mm